Latamid 6 H2 G/30-V0CT1
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QW7YNd_Latamid-6-H2-G-30-V0CT1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 6 (PA 6). Heat stabilised. Glass fibres. UL94 V-0 classified, with halogens, PBB/PBDE free. Product UL certified. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.54 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.50 to 0.70 | % | |
| Flow : 2.00 mm | 0.25 to 0.45 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 11000 | MPa | |
| 60°C | 7400 | MPa | |
| 90°C | 5100 | MPa | |
| 120°C | 4200 | MPa | |
| 150°C | 3600 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 125 | MPa | |
| Break, 60°C | 80.0 | MPa | |
| Break, 90°C | 60.0 | MPa | |
| Break, 120°C | 50.0 | MPa | |
| Break, 150°C | 40.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 2.0 | % | |
| Break, 60°C | 4.5 | % | |
| Break, 90°C | 6.0 | % | |
| Break, 120°C | 7.0 | % | |
| Break, 150°C | 7.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 7.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 35 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 90 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 215 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 185 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 95.0 | °C | |
| Vicat Softening Temperature | 195 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 400 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 800 | °C | |
| 2.00 mm | 800 | °C | |
| Oxygen Index | 28 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 70.0 to 100 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® HDPE M200056 | Saudi Basic Industries Corporation (SABIC) | HDPE Copolymer | SABIC® HDPE |
| UmaPET IT | Ester Industries Ltd. | PET | UmaPET |
| Braskem PE HE 150 | Braskem | HDPE | Braskem PE |
| Hyundai EP PPF HT121 | HYUNDAI EP Co., Ltd. | PP Homopolymer | Hyundai EP PPF |
| Sylvin 9077-90 Grey 9225 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |