Versaflex™ HC 2110-43N
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Versaflex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QVNAwH_Versaflex-HC-2110-43N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Versaflex™ HC 2110-43N is a unique TPE designed for the demanding requirements of pharmaceutical packaging. New Product. Commercial specifications have not been established.
|
| General Information | |
|---|---|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.978 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 10 sec) | 43 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain, 23°C | 0.924 | MPa | ASTM D412 |
| 300% strain, 23°C | 2.54 | MPa | ASTM D412 |
| Tensile Strength (Break, 23°C) | 4.98 | MPa | ASTM D412 |
| Tensile Elongation (Break, 23°C) | 710 | % | ASTM D412 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 12 | % | ASTM D395B |
| 70°C, 22 hr | 22 | % | ASTM D395B |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity | ASTM D3835 | ||
| 200°C, 1340 sec^-1 | 52.7 | Pa·s | ASTM D3835 |
| 200°C, 11200 sec^-1 | 10.5 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 171 - 193 | °C | |
| Middle Temperature | 193 - 243 | °C | |
| Front Temperature | 204 - 254 | °C | |
| Nozzle Temperature | 216 - 254 | °C | |
| Mold Temperature | 15.6 - 37.8 | °C | |
| Back Pressure | 0.00 - 0.827 | MPa | |
| Screw Speed | 25 - 100 | rpm |
| Injection instructions |
|---|
| 在使用此产品之前或之后，均须用熔体流动速率较低 (0.5 - 2.5 MFR) 的聚乙烯 (PE) 或聚丙烯 (PP) 彻底进行置换。Versaflex™ HC 2110-43N 具有极好的熔体稳定性。最长停留时间可能会根据机筒尺寸有所变化。通常，如果机器闲置 8 - 10 分钟或以上，则应将机筒排空。不需要干燥注射速度：1 - 3 英寸/秒第一阶段 - 提升压力：25 - 1000 psi第二阶段 - 保持压力：30% 的升压保持时间（厚部件）：3 - 10 秒保持时间（薄部件）：1 - 3 秒 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEKAMID™ TB120GM40 | Mando Advanced Materials Co., Ltd. | Nylon 6 | TEKAMID™ |
| Taitacell EPS-351T | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Xmod™ WD300UBB | Borealis AG | TPO | Xmod™ |
| NYLOY® UB-0010N G50L1N | Nytex Composites Co., Ltd. | Nylon, Unspecified | NYLOY® |
| StarGrip-X® 5045-1000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarGrip-X® |