LubriOne™ SF-30CF/15T BLACK
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | PolyOne Corporation |
| Trademark: | LubriOne™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QUeI0H_LubriOne-SF-30CF-15T-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PTFE lubricated |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.15 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 13500 | MPa | ASTM D638 |
| Tensile Strength 2 | 138 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 2.0 | % | ASTM D638 |
| Flexural Modulus 4 | 15000 | MPa | ASTM D790 |
| Flexural Strength 5 | 210 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 70 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 260 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 50 - 1.0E+3 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 - 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 320 - 330 | °C | |
| Middle Temperature | 320 - 330 | °C | |
| Front Temperature | 320 - 330 | °C | |
| Mold Temperature | 140 - 160 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E195 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| SOLLAMID B 2700 FV 35 | Krisoll Resinas Plásticas Ltda. | Nylon 6 | SOLLAMID |
| SPI HOPP12 | Service Polymers, Inc. | PP Homopolymer | SPI |
| Viton® C-10 | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| Nypol® PA A3 G38 HS UV RH PRTA011 NR447 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |