PLEXIGLAS® Resist zk40 is an amorphous, impact-modified thermoplastic molding compound (PMMA-I).

Typical properties of impact-modified PLEXIGLAS® molding compounds are

excellent transmission and clarity

brilliant appearance

the pleasant feel and sound of the moldings.

PLEXIGLAS® Resist zk40 is characterized by the following special properties:

very good break resistance and impact strength

improved resistance to stress cracking

AMECA listing.

Application:
Used for injection molding. Profile extrusion or coextrusion are also possible.

Examples:
lighting fixtures, writing and drawing utensils, domestic appliances and sanitaryware

General Information
Additive	Impact Modifier
Features	High Clarity High ESCR (Stress Crack Resist.) High Impact Resistance Pleasing Surface Appearance
Uses	Appliances Flexible Grips Profiles Sanitary Products Writing Instruments
Forms	Pellets
Processing Method	Coextrusion Extrusion Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density	1.13	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (230°C/3.8 kg)	0.700	cm³/10min	ISO 1133
Water Absorption (Equilibrium, 23°C, 50% RH)	0.38	%	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	1600	MPa	ISO 527-2/1
Tensile Stress (Yield)	42.0	MPa	ISO 527-2/50
Tensile Strain (Yield)	4.5	%	ISO 527-2/50
Nominal Tensile Strain at Break	30	%	ISO 527-2

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	80	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	92.0	°C	ISO 75-2/B
1.8 MPa, Unannealed	85.0	°C	ISO 75-2/A
Glass Transition Temperature	115	°C	ISO 11357-2
Vicat Softening Temperature	94.0	°C	ISO 306/B50
CLTE - Flow (0 to 50°C)	1.2E-4	cm/cm/°C	ISO 11359-2

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.490		ISO 489
Transmittance ¹	90.0	%	ISO 13468-2

Injection	Nominal Value	Unit
Drying Temperature	< 84.0	°C
Drying Time	2.0 to 3.0	hr
Processing (Melt) Temp	230 to 240	°C
Mold Temperature	50.0 to 70.0	°C

Note Message
1 .	D65

Resin Grade	Manufacturer	Category	Trademark
TUFLIN™ HS-7098C NT 7	The Dow Chemical Company	LLDPE	TUFLIN™
AKROMID® B3 GF 30 natural (2472)	AKRO-PLASTIC GmbH	Nylon 6	AKROMID®
DJSilicone NE-9140	DONGJUE SILICONE (NANJING) CO., LTD	Silicone	DJSilicone
HAIPLEN EP70 Y0	Taro Plast S.p.A.	PP Copolymer	HAIPLEN
ESTACARB 1060 V0 HF	Cossa Polimeri S.r.l.	PC	ESTACARB