Retpol® PDR 1629 HS
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QU3xLI_Retpol-PDR-1629-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| CORTON PDR 1629 HS is a 35 % wollastonite filled homopolymer polypropylene compound. It is a medium to high flow injection moulding grade developed for rigid components. It has been stabilized to meet heat aging requirements of 21 days at 150°C. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.50 to 0.90 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 98 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 80 | ||
| Shore D, 15 sec, 3.00 mm | 71 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 32.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 16 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 4900 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.00 mm) | 29 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.00 mm) | 280 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.00 mm | 130 | °C | |
| 1.8 MPa, Unannealed, 3.00 mm | 82.0 | °C | |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NOVAPOLY 0225UV | NOVA Polymers, Inc. | PC Alloy | NOVAPOLY |
| Latamid 66 H2 G/50-GWHF1 | LATI S.p.A. | Nylon 66 | Latamid |
| Jiangsu Sinarise JM8211 | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |
| MAJORIS PBT 9237 20 M BLACK 8229 | AD majoris | PBT | MAJORIS |
| Hostacom X M2 V05 M C11462 | LyondellBasell Industries | PP Copolymer | Hostacom |