LUVOCOM® 1850-7581 Datasheet,PBT,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®1850-7581 is a polybutene terephthalate (PBT) material, and the filler is carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. LUVOCOM®The main features of 1850-7581 are: Conductivity Electrostatic protection Lubrication Typical application areas include: Electrical/electronic applications Reflector textile/fiber engineering/industrial accessories Automotive Industry

General Information
Filler / Reinforcement	Carbon fiber reinforced material
Additive	PTFE lubricant
Features	Conductivity Electrostatic discharge protection Lubrication
Uses	Electrical/Electronic Applications Reflector Textile applications Engineering accessories Switch Application in Automobile Field Business equipment spool
Appearance	Black

Physical	Nominal Value	Unit	Test Method
Density	1.52	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (250°C/5.0 kg)	11.0	cm³/10min	ISO 1133
Molding Shrinkage	0.10 - 0.40	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	20000	MPa	ISO 527-2
Tensile Stress (Break)	140	MPa	ISO 527-2
Tensile Strain (Yield)	1.3	%	ISO 527-2
Flexural Modulus	17000	MPa	ISO 178
Flexural Stress	195	MPa	ISO 178
Coefficient of Friction
Dynamic	0.14
Static	0.10
Flexural Strain at Flexural Strength	1.6	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	180	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	30	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	210	°C	ISO 75-2/A
Continuous Use Temperature	130	°C	UL 746B
Vicat Softening Temperature	210	°C	ISO 306/A

Injection	Nominal Value	Unit
Drying Temperature
A	120	°C
Vacuum dryer, B	80.0	°C
Drying Time
A	4.0 - 6.0	hr
Vacuum dryer, B	6.0 - 8.0	hr
Suggested Max Moisture	0.020	%
Rear Temperature	240 - 260	°C
Middle Temperature	260 - 280	°C
Front Temperature	250 - 270	°C
Nozzle Temperature	250 - 265	°C
Processing (Melt) Temp	250	°C
Mold Temperature	60.0 - 120	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	QTIgtq_LUVOCOM-1850-7581.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Razamid® A111	Razin™ Engineering Plastics	Nylon 66	Razamid®
DINALON® A3S25-0042	Grupo Repol	Nylon 66	DINALON®
Kumho SSBR SOL-C6450SL	Korea Kumho Petrochemical Co., Ltd.	SBR, Solution	Kumho SSBR
LubriOne™ PC-10GF/15T BLACK	PolyOne Corporation	PC	LubriOne™
Lusin® Clean G 295 C	Chem-Trend L.P.	Unspecified	Lusin®