POLYLAC® PA-765A
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | CHI MEI CORPORATION |
| Trademark: | POLYLAC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QSkhRt_POLYLAC-PA-765A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLYLAC® PA-765A is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 4.6 | g/10 min | |
| 220°C/10.0 kg | 46 | g/10 min | |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 46.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 101 | ASTM D785 | |
| Ball Indentation Hardness (H 358/30) | 81.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 40.0 | MPa | ISO 527-2/50 |
| Break | 28.0 | MPa | ISO 527-2/50 |
| 3.00 mm 1 | 39.2 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Break, 3.00 mm 2 | 20 | % | ASTM D638 |
| Break | 10 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 6.00 mm 3 | 2260 | MPa | ASTM D790 |
| -- 4 | 1700 | MPa | ISO 178 |
| Flexural Strength | |||
| 6.00 mm 5 | 62.8 | MPa | ASTM D790 |
| -- 6 | 54.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 20 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C, 3.00 mm | 240 | J/m | ASTM D256 |
| 23°C, 6.00 mm | 200 | J/m | ASTM D256 |
| -- | 19 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 76.0 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, Annealed | 85.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed | 91.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 92.0 | °C | ASTM D1525 7 |
| -- | 90.0 | °C | ISO 306/A50 |
| -- | 79.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 2.00 mm | V-0 | ||
| 2.10 mm | V-0 | ||
| 2.50 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 85.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 180 to 210 | °C | |
| Middle Temperature | 190 to 220 | °C | |
| Front Temperature | 190 to 220 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Injection Pressure | 4.90 to 7.85 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 1.96 to 4.90 | MPa | |
| Back Pressure | 0.490 to 0.981 | MPa | |
| Cushion | 3.18 | mm |
| Note Message | |
|---|---|
| 1 . | 6.0 mm/min |
| 2 . | 6.0 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultrason® E 3010 MR UN | BASF Corporation | PESU | Ultrason® E |
| NORYL GTX™ GTX678 resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |
| Ad-Tech Epoxy EL-322 | Ad-Tech Plastic Systems Corp. | Epoxy | Ad-Tech Epoxy |
| Aurora PVC AP1260 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| Hyflon® PFA P120X | Solvay Specialty Polymers | PFA | Hyflon® PFA |