Orgalloy® LT 5050

Category:	Nylon 6 Alloy , Polyamide 6 Alloy
Manufacturer:	Arkema
Trademark:	Orgalloy®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	QSgyW0_Orgalloy-LT-5050.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Orgalloy® LT 5050 is a Polyamide 6 Alloy (Nylon 6 Alloy) product. It can be processed by calendering, extrusion, film extrusion, injection molding, profile extrusion, resin transfer molding, sheet extrusion, or thermoforming and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America.

Characteristics include:

Heat Resistant

Impact Resistant

General Information
Features	Good Impact Resistance High Heat Resistance Platable
Forms	Pellets
Processing Method	Calendering Extrusion Film Extrusion Injection Molding Profile Extrusion Resin Transfer Molding Sheet Extrusion Thermoforming
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Dry	Conditioned	Unit	Test Method
Density	1040	1040	kg/m³	ISO 1183 ¹
Melt volume-flow rate (235°C/5.0 kg)	2.00	--	cm³/10min	ISO 1133 ²

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile modulus	--	460	MPa	ISO 527-2 ³
Tensile Stress (50% Strain)	--	23.0	MPa	ISO 527-2 ⁴
Tensile Strain (Break)	--	> 50	%	ISO 527-2 ⁵
Tensile Creep Modulus				ISO 899-1 ⁶
1 hr	--	420	MPa
1000 hr	--	270	MPa

Thermal	Dry	Conditioned	Unit	Test Method
Melting Temperature ⁷	220	--	°C	ISO 11357-3 ⁸
CLTE				ISO 11359-2 ⁹
Flow	1.7E-4	--	cm/cm/°C
Transverse	1.8E-4	--	cm/cm/°C

Electrical	Dry	Conditioned	Unit	Test Method
Surface resistivity	--	> 1.0E+15	ohms	IEC 60093 ¹⁰
Volume resistivity	--	7.5E+11	ohms·m	IEC 60093 ¹¹
Electric strength	36	36	kV/mm	IEC 60243-1 ¹²
Relative Permittivity				IEC 60250 ¹³
100 Hz	--	4.00
1 MHz	--	4.00
Dissipation Factor				IEC 60250 ¹⁴
100 Hz	--	0.11
1 MHz	--	0.050
Comparative tracking index	--	600		IEC 60112 ¹⁵

Flammability	Dry	Conditioned	Unit	Test Method
Burning Behav. at 1.6mm nom. thickn. (1.60 mm)	HB	--		ISO 1210 ¹⁶
Burning Behav. at thickness h (3.20 mm)	HB	--		ISO 1210 ¹⁷

Note Message
1 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
2 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
3 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
4 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
5 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
6 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
7 .	10 °C/min
8 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
9 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
10 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
11 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
12 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
13 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
14 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
15 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
16 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
17 .	Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.

Resin Grade	Manufacturer	Category	Trademark
Celcon® GB10	Celanese Corporation	Acetal (POM) Copolymer	Celcon®
Exelene® LLDPE 2601	Montachem International, Inc.	LLDPE	Exelene® LLDPE
Ferro PP TPP20AF70UL	Ferro Corporation	PP Homopolymer	Ferro PP
Geon™ Vinyl Rigid Molding M3890	PolyOne Corporation	PVC, Rigid	Geon™ Vinyl Rigid Molding
Elvax® 3178Z	DuPont Packaging & Industrial Polymers	EVA	Elvax®