ACCUTECH™ HP0336W10L1
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | ACLO Compounders Inc. |
| Trademark: | ACCUTECH™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QS3YQ9_ACCUTECH-HP0336W10L1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ACCUTECH™HP0336W10L1 is a polypropylene homopolymer (PP Homopoly) product containing 10% wollastonite (casio3). It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.958 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.1 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 89 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1600 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield | 34.0 | MPa | ASTM D638 |
| Fracture | 25.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 25 | % | ASTM D638 |
| Flexural Modulus | 1500 | MPa | ASTM D790 |
| Flexural Strength | 37.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 44 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 108 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 61.0 | °C | ASTM D648 |
| Additional Information |
|---|
| Ash Content, ASTM D2584: 10% |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene F52-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| SLOVALEN® PC 82 T 30 | Plastcom | PP, Unspecified | SLOVALEN® |
| VITAMIDE® BR3XNT6509 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Boda BDF-KR2852 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| Elastamax™ HTE 1105 | PolyOne Corporation | SBC | Elastamax™ |