Riblene® FL 30 I
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Riblene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QRxcwe_RibleneFL30I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Riblene FL 30 I is a low density polyethylene (LDPE) ideal for blown film extrusion. Riblene FL 30 is characterised by a good balance between processability, mechanical and optical properties. Films manufactured by Riblene FL 30 are easily heat shrinkable. Main Applications Riblene FL 30 I, due to its low gels level, is recommended for general blown film applications, for the production of low gauge film , shrink film, in lamination film and for blend. Thanks its high purity is also recommended for the production in hygienical and pharmaceutical film sector. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.2 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Film Thickness - Recommended / Available | 25 to 80 µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% secant, MD : 40 µm, blown film | 180 | MPa | ISO 527-3 |
| 1% secant, TD : 40 µm, blown film | 190 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 40 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD : Yield, 40 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD : Broken, 40 µm, blown film | 25.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 22.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 300 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 650 | % | ISO 527-3 |
| Dart Drop Impact 1(40 µm, Blown Film) | 130 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 40.0 µm | 80.0 | kN/m | ISO 6383-2 |
| TD : 40.0 µm | 55.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -75.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 93.0 | °C | ISO 306/A |
| Melting Temperature | 113 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 72 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 5.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 - 190 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2956-80 Green 3171 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Ultramid® A3WG10 BK00564 | BASF Corporation | Nylon 66 | Ultramid® |
| Karina RED COLOR CONCENTRATE -E 42/183-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OxyShield® 2545 | Honeywell | Nylon 6 | OxyShield® |
| Sylvin 5132-75 Clear Black 282 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |