G-PAEK™ 1300G
| Category: | PEK , Polyether Ketone |
| Manufacturer: | Gharda Chemicals Ltd. |
| Trademark: | G-PAEK™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QRhyoD_G-PAEK-1300G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product Details: Ultra high Performance thermoplastic polymer, virgin, semicrystalline granules suitable for Injection Molding, easy flow, Beige in color. Application Areas: Suitable for high temperature application, high wear & abrasion resistance, high chemical resistance is required & for metal replacement with plastics etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | |
| Spiral Flow 1 | 53.0 | cm | ASTM D3123 |
| Molding Shrinkage 2 | |||
| Flow | 1.1 | % | |
| Across Flow | 1.4 | % | |
| Water Absorption (Equilibrium) | 0.070 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 98 | ASTM D785 | |
| Durometer Hardness (Shore D) | 87 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4300 | MPa | ASTM D638 |
| Tensile Strength (Yield, 23°C) | 90.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 4.0 to 6.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 4300 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 163 | MPa | ASTM D790 |
| Compressive Strength | 130 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 35 | J/m | ASTM D256 |
| Unnotched Izod Impact | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 175 | °C | ASTM D648 |
| Continuous Use Temperature | 280 | °C | UL 746B |
| Glass Transition Temperature | 152 | °C | ASTM D3418 |
| Melting Temperature | 372 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | V-0 | UL 94 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C, 1000 sec^-1) | 200 to 250 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Nozzle Temperature | 400 | °C | |
| Processing (Melt) Temp | 390 to 400 | °C | |
| Mold Temperature | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 400°C nozzle, 220°C Mold |
| 2 . | 400°C nozzle, 210°C Mold |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 5145-80 CLEAR YELLOW 4112 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Vital-Line SHM6005 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Adiprene® LFP 3940A | Chemtura | PUR-PC/PPDI | Adiprene® |
| Karina WHITE PVC COMPOUND -E 837-10/168-A-ERYB-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Dapol® D2102F | Fudow Co., Ltd. | DAP | Dapol® |