VICTREX® PEEK 450GL30
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Victrex plc |
| Trademark: | VICTREX® PEEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QQGLgt_VICTREX-PEEK-450GL30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High performance thermoplastic material, 30% glass fibre reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, standard flow, FDA food contact compliant, colour natural/beige. Applications for higher strength in a static system. Low coefficient of thermal expansion. Chemically resistant to aggressive environments, suitable for sterilisation for medical and food contact applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Spiral Flow 1 | Internal method | ||
| -- 2 | 8.50 | cm | Internal method |
| -- 3 | 41.0 | cm | Internal method |
| Molding Shrinkage | |||
| Vertical flow direction : 190°C 4 | 0.90 | % | |
| Flow direction : 190°C 5 | 0.30 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.20 mm | 0.040 | % | ISO 62 |
| Balance, 23°C, 3.20mm, 50% RH | 0.30 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 88 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 11800 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Fracture, 23°C | 180 | MPa | ISO 527-2 |
| Fracture, 125°C | 115 | MPa | ISO 527-2 |
| Fracture, 175°C | 60.0 | MPa | ISO 527-2 |
| Fracture, 275°C | 35.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 2.7 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 11300 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| 23°C | 270 | MPa | ISO 178 |
| 125°C | 190 | MPa | ISO 178 |
| 175°C | 80.0 | MPa | ISO 178 |
| 275°C | 50.0 | MPa | ISO 178 |
| Compressive Stress | ISO 604 | ||
| 23°C | 250 | MPa | ISO 604 |
| 120°C | 160 | MPa | ISO 604 |
| 200°C | 55.0 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 55 | kJ/m² | ISO 179/1U |
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength (23°C) | 60 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 328 | °C | ISO 75-2/A |
| Glass Transition Temperature | 143 | °C | ISO 11357-2 |
| Melting Temperature | 343 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : > 143°C | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : < 143°C | 1.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : < 143°C | 4.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : > 143°C | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Specific Heat (23°C) | 1700 | J/kg/°C | DSC |
| Thermal Conductivity (23°C) | 0.30 | W/m/K | ISO 22007-4 |
| RTI Elec | 240 | °C | UL 746 |
| RTI Imp | 220 | °C | UL 746 |
| RTI | 240 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength (2.00 mm) | 25 | kV/mm | IEC 60243-1 |
| Dielectric Constant (23°C, 2 MHz) | 3.20 | IEC 60250 | |
| Dissipation Factor (23°C, 1 MHz) | 5.0E-3 | IEC 60250 | |
| Comparative Tracking Index | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C) | 560 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Hopper Temperature | < 100 | °C | |
| Rear Temperature | 365 | °C | |
| Middle Temperature | 370 - 375 | °C | |
| Front Temperature | 380 | °C | |
| Nozzle Temperature | 385 | °C | |
| Mold Temperature | 180 - 200 | °C |
| Injection instructions |
|---|
| Runner: Die / nozzle >3mm, manifold >3.5mmGate: >2mm or 0.5 x part thickness |
| Note Message | |
|---|---|
| 1 . | Mold temperature: 190°C, melt temperature: 385°C |
| 2 . | 1 mm |
| 3 . | 3 mm |
| 4 . | 385°C nozzle, |
| 5 . | 385°C nozzle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8716-95 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Arak LLDPE LL0220AA | Shazand (Arak) Petrochemical Corporation | LLDPE | Arak LLDPE |
| Axiall PVC 6741 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| OTECH TPO OTO9588 - Automotive | OTECH Corporation | TPO | OTECH TPO |
| Sylvin 8600-85 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |