ALCOM® PC 740/4 UV WT1220-05LD
| Category: | PC , Polycarbonate |
| Manufacturer: | ALBIS PLASTIC GmbH |
| Trademark: | ALCOM® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QQ1w1L_ALCOM-PC-740-4-UV-WT1220-05LD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCOM® PC 740/4 UV WT1220-05LD is a Polycarbonate (PC) product filled with filler. It is available in Asia Pacific, Europe, or North America. Applications of ALCOM® PC 740/4 UV WT1220-05LD include automotive and lighting applications. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 17.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.40 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 66.0 | MPa | |
| -- | 66.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 6.0 | % | |
| Break | 70 | % | |
| Flexural Modulus | 2450 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | ||
| -- | 100 | MPa | |
| 3.5% Strain | 76.0 | MPa | |
| Flexural Deflection at Max Force | 7.0 | % | ISO 178 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fire Performance (1.00 mm) | passed | FMVSS |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Half Power Angle - T(Y) 1(1.00 mm) | 52.0 | ° |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -- | 12 | kJ/m² | |
| -40°C | 12 | kJ/m² | |
| -20°C | 12 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -- | No Break | ||
| -40°C | No Break | ||
| -20°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 124 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 142 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 0.750 mm | V-2 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 850 | °C | |
| 2.00 mm | 850 | °C | |
| 3.00 mm | 850 960 | °C | |
| 4.00 mm | 960 850 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance 2(Total, 1000 µm) | 55.0 | % | ISO 13468 |
| Haze 3(1000 µm) | 95 | % | ISO 13468 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 4.0 to 12 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 270 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | A, 2° |
| 2 . | A, 2° |
| 3 . | Ill. A, 2° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ B70 G25 BK034 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Altuglas® BS 520 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| Geon™ Vinyl Flexible R323AE | PolyOne Corporation | PVC Elastomer | Geon™ Vinyl Flexible |
| LITEN BB 29 H | UNIPETROL RPA | LPE Copolymer | LITEN |
| Plenco 02482 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |