LEXAN™ LUX2614G resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QPmMc9_LEXAN-LUX2614G-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN LUX2614G (EXRL0944) is a diffusive, high viscosity, uv stabilized, flame retardant polycarbonate with improved light transmission and providing good colorstability under heat exposure. Developed for injection molding LED applications |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.20 | g/cm³ | |
| -- | 1.19 | g/cm³ | |
| Specific Volume | 0.830 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 7.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.70 | % | Internal Method |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.15 | % | |
| Equilibrium, 23°C | 0.35 | % | |
| Equilibrium, 100°C | 0.58 | % | |
| Outdoor Suitability | f2 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 70 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 1 | 62.1 | MPa | ASTM D638 |
| Yield | 63.0 | MPa | ISO 527-2/50 |
| Break 2 | 65.5 | MPa | ASTM D638 |
| Break | 63.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 3 | 7.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 4 | 110 | % | ASTM D638 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 2340 | MPa | ASTM D790 |
| -- 6 | 2300 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 94.0 | MPa | ISO 178 |
| Yield, 50.0 mm Span 7 | 93.1 | MPa | ASTM D790 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 10.0 | mg | ASTM D1044 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 750 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 3200 | J/m | ASTM D4812 |
| Gardner Impact (23°C) | 169 | J | ASTM D3029 |
| Tensile Impact Strength 8 | 546 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 138 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 132 | °C | |
| Vicat Softening Temperature | |||
| -- | 154 | °C | ASTM D1525 9 |
| -- | 145 | °C | ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| CLTE - Flow (-40 to 95°C) | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Specific Heat | 1260 | J/kg/°C | ASTM C351 |
| Thermal Conductivity | 0.29 | W/m/K | ASTM C177 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 125 | °C | UL 746 |
| RTI Str | 125 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Air) | 15 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.17 | ||
| 60 Hz | 3.17 | ||
| 1 MHz | 2.96 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 9.0E-4 | ||
| 60 Hz | 9.0E-4 | ||
| 1 MHz | 0.010 | ||
| Comparative Tracking Index (CTI) | PLC 3 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 3 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 to 3.00 mm) | V-2 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.750 mm | 750 | °C | |
| 1.50 mm | 850 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.750 mm 10 | 875 | °C | |
| 1.50 mm | 850 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance (2540 µm) | 88.0 | % | ASTM D1003 |
| Haze (2540 µm) | 1.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 60 | % | |
| Rear Temperature | 288 to 310 | °C | |
| Middle Temperature | 299 to 321 | °C | |
| Front Temperature | 310 to 332 | °C | |
| Nozzle Temperature | 304 to 327 | °C | |
| Processing (Melt) Temp | 310 to 332 | °C | |
| Mold Temperature | 82.2 to 116 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.025 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | Type I, 50 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | Type S |
| 9 . | Rate B (120°C/h), Loading 2 (50 N) |
| 10 . | by VDE |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYshine PBT D611 | Polykemi AB | PBT | POLYshine |
| Polymist® F5A | Solvay Specialty Polymers | PTFE | Polymist® |
| Iupital® F20-03 | Mitsubishi Engineering-Plastics Corp | Acetal (POM) Copolymer | Iupital® |
| ISOPAK® 625 | Great Eastern Resins Industrial Co Ltd (GRECO) | PC+ABS | ISOPAK® |
| PLUSTEK RB133 | Polyram Ram-On Industries | Nylon 6 | PLUSTEK |