UNIBRITE® UB-700A
| Category: | AES , Acrylonitrile Ethylene Styrene |
| Manufacturer: | Nippon A&L Inc. |
| Trademark: | UNIBRITE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QPh5PF_UNIBRITE-UB-700A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UNIBRITE®UB-700A is an acrylonitrile ethylene styrene (AES) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. UNIBRITE®The main characteristics of the UB-700A are: impact resistance. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.04 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.60 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 108 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 47.0 | MPa | ISO 527-2 |
| Flexural Modulus (23°C) | 2250 | MPa | ISO 178 |
| Flexural Stress (23°C) | 73.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 45 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 80.0 | °C | ISO 75-2/A |
| CLTE - Flow (23 to 80°C) | 8.5E-5 | cm/cm/°C | JIS K7197 |
| Additional Information |
|---|
| Ball Pressure Registration Temperature: 90°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | > 3.0 | hr | |
| Rear Temperature | 200 - 260 | °C | |
| Middle Temperature | 200 - 260 | °C | |
| Front Temperature | 200 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDILENE J 520 T30 | ADDIPLAST | PP Copolymer | ADDILENE |
| FERREX® GPP40CC90UL | Ferro Corporation | PP Homopolymer | FERREX® |
| EMLON® 66 GFR 35 | EMAS Plastik San.Tic.AS. | Nylon 66 | EMLON® |
| Latamid 6 H2 G/30-V0HF1 | LATI S.p.A. | Nylon 6 | Latamid |
| INSTRUC PA66GF10 | Infinity LTL Engineered Compounds | Nylon 66 | INSTRUC |