Aegis® H155ZP
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Honeywell |
| Trademark: | Aegis® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QPY38c_Aegis-H155ZP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Aegis® H155ZP is a high viscosity nylon 6 extrusion grade homopolymer for cast or blown film. It conforms to FDA requirements of 21 CFR 177.1500 as well as EU Directive 2002/72/EC. It possesses the combination of strength, toughness and thermoforming properties associated with nylon 6 as well as excellent heat, chemical, and abrasion resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (235°C/1.0 kg) | 1.1 | g/10 min | ASTM D1238 |
| Water Absorption | ASTM D570 | ||
| 24 hr | 1.6 | % | ASTM D570 |
| Saturation | 9.5 | % | ASTM D570 |
| Balance, 50% RH | 2.7 | % | ASTM D570 |
| Moisture Content | % | ASTM D6869 | |
| Relative viscosity- @ 96% Sulfuric Acid | 4.00 | ||
| Viscosity- FAV | 155 | ASTM D789 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 23°C | 1130 | N | ASTM D1922 |
| TD : 23°C | 750 | N | ASTM D1922 |
| Graves Tear | ASTM D1004 | ||
| MD : 23°C | 2760 | N | ASTM D1004 |
| TD : 23°C | 2520 | N | ASTM D1004 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Puncture Index (23°C) 1 | 193.0 | kN/m | |
| Puncture Resistance (23°C) 2 | 940 | g |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Elastic Modulus - MD 3 | 650 | MPa | ASTM D882 |
| Elastic Modulus - TD 4 | 590 | MPa | ASTM D882 |
| Tensile Strength 5 | ASTM D882 | ||
| MD : Yield | 30.0 | MPa | ASTM D882 |
| TD : Yield | 30.0 | MPa | ASTM D882 |
| MD : Fracture | 80.0 | MPa | ASTM D882 |
| TD : Fracture | 60.0 | MPa | ASTM D882 |
| Tensile Elongation 6 | ASTM D882 | ||
| MD : Fracture | 310 | % | ASTM D882 |
| TD : Fracture | 280 | % | ASTM D882 |
| Carbon Dioxide Transmission Rate (23°C) | 72.8 | cm³/m²/24 hr | ASTM D1434 |
| Nitrogen Transmission Rate (23°C) | 14.0 | cm³/m²/24 hr | ASTM D1434 |
| Oxygen Transmission Rate (23°C) | 40 | cm³/m²/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate (38°C, 100% RH) | 990 | g/m²/24 hr | ASTM F1249 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Melting Temperature | 220 | °C |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Extractible Content: 0.7 % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Cylinder Zone 1 Temp. | 230 - 260 | °C | |
| Cylinder Zone 2 Temp. | 230 - 260 | °C | |
| Cylinder Zone 3 Temp. | 230 - 260 | °C | |
| Cylinder Zone 4 Temp. | 230 - 260 | °C | |
| Cylinder Zone 5 Temp. | 230 - 260 | °C | |
| Adapter Temperature | 260 - 266 | °C | |
| Melt Temperature | 260 - 270 | °C | |
| Die Temperature | 260 | °C |
| Extrusion instructions |
|---|
| The values listed above in Extrusion are for cast film.Typical Barrel Profile for Tubular (Blown) Films: Barrel Temperature: 246 to 254°C (474 to 490°F) Adapter Temperature: 260°C (500°F) Die Temperature: 254°C (490°F) Processing Melt Temperature: 254 to 260°C (490 to 500°F) Screw Parameters: Metering section: 40% Transition section: 3 to 4 flights Feed section balance of screw length Compression ratio: 3.5:1 to 4.0:1 L/D ratio: 24:1 |
| Note Message | |
|---|---|
| 1 . | ASTM D1306 |
| 2 . | ASTM D1306 |
| 3 . | 23°C |
| 4 . | 23°C |
| 5 . | 23°C |
| 6 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® PVC VSS-F110 | Sumitomo Bakelite Co., Ltd. | PVC, Unspecified | SUMILITE® PVC |
| NITRIFLEX S-6H | NITRIFLEX | SBR, Unspecified | NITRIFLEX |
| Fainplast PVC RK 115 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Hanwha Total PP RF401 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Infino WP-1059 | LOTTE ADVANCED MATERIALS CO., LTD. | PC+ABS | Infino |