Spartech Polycom X03321
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QPKiwv_Spartech-Polycom-X03321.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% Calcium Carbonate FIlled Extrusion Grade, Black , coumpound offers a high level of stiffness and heat deflection performance balanced with excellent processibility. The nominal melt flow of 1.0 g/10 min. makes this product ideal for sheet extrusion thermoforming applications up to 100 mil thickness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 31.0 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.0 | % | ASTM D638 |
| Fracture | 40 | % | ASTM D638 |
| Flexural Modulus - Secant | 1590 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 1.58 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 98.9 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 54.4 | °C | ASTM D648 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 75 | ASTM D523 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Wanthane® WHT-A890 | Wanhua Chemical Group Co., Ltd. | TPU-Polyether | Wanthane® |
| NEXUS PE HDPE-00649 | Nexus Resin Group, LLC. | HDPE | NEXUS PE |
| Allen ABS 3800/LXS | SEKISUI Polymer Innovations, LLC | ABS | Allen ABS |
| Magnobond 3265 | Magnolia Plastics, Inc. | Epoxy | Magnobond |
| Polybutene-1 DP 8220M | LyondellBasell Industries | PB | Polybutene-1 |