LNP™ THERMOCOMP™ Lexan_BFL2200 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QOUmc5_LNP-THERMOCOMP-Lexan-BFL2200-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| design for black light frame application as high flow PC, V-2, high reflection grade. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 36 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 36.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.74 to 0.76 | % | Internal Method |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.20 | % | |
| Equilibrium, 23°C, 50% RH | 0.10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2600 | MPa | ASTM D638 |
| -- | 2.54 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 55.0 | MPa | ASTM D638 |
| Yield | 55.6 | MPa | ISO 527-2/5 |
| Break 3 | 50.2 | MPa | ASTM D638 |
| Break | 47.9 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.4 | % | ASTM D638 |
| Yield | 5.4 | % | ISO 527-2/5 |
| Break 5 | 59 | % | ASTM D638 |
| Break | 48 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2220 | MPa | ASTM D790 |
| -- 7 | 2.34 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.2 | MPa | ISO 178 |
| Yield, 50.0 mm Span 8 | 84.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 35 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 160 | J/m | ASTM D256 |
| 23°C | 550 | J/m | ASTM D256 |
| -30°C 10 | 16 | kJ/m² | ISO 180/1A |
| 23°C 11 | 30 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 125 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 172 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 144 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 147 | °C | ISO 306/B120 |
| CLTE | |||
| Flow : -40 to 40°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 6.1E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 6.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TF4BNA (Series: FC/AP) | KRAIBURG TPE | TPE | THERMOLAST® K |
| GELAST GT807CA | Guang Sung Plastics (GSPL) | SEBS | GELAST |
| Geon™ Vinyl Flexible R7545H | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Hipolyene 3020 HC RM | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Lupolen 4261 AG BD | LyondellBasell Industries | HDPE, HMW | Lupolen |