| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Blueridge Films Inc. |
| Trademark: | BFI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QO4dPg_BFI-6420.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BFI 6420 is a High Density Polyethylene material. It is available in North America. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.960 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 2.0 | g/10 min | |
| 190°C/21.6 kg | 55 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus 1 | ASTM D882A | ||
| 1% Secant, MD : Blown Film | 0.862 | MPa | |
| 2% Secant, MD : Blown Film | 0.689 | MPa | |
| 1% Secant, TD : Blown Film | 0.883 | MPa | |
| 2% Secant, TD : Blown Film | 0.703 | MPa | |
| Tensile Strength 2 | ASTM D882A | ||
| MD : Yield, Blown Film | 26.2 | MPa | |
| TD : Yield, Blown Film | 27.6 | MPa | |
| MD : Break, Blown Film | 51.7 | MPa | |
| TD : Break, Blown Film | 23.4 | MPa | |
| Tensile Elongation 3 | ASTM D882A | ||
| MD : Break, Blown Film | 700 | % | |
| TD : Break, Blown Film | 700 | % | |
| Dart Drop Impact (Blown Film) | 100 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : Blown Film | 24 | g | |
| TD : Blown Film | 390 | g | |
| Water Vapor Transmission Rate (38°C, Blown Film) | 0.098 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Note Message | |
|---|---|
| 1 . | 25 mm/min |
| 2 . | 51 mm/min |
| 3 . | 51 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene G13P100-347UV | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Starex VH-0800 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Badadur® PBT8 S | Bada AG | PBT | Badadur® |
| DynaPath™ C2045CFT | Polymer Dynamix | Nylon 66 | DynaPath™ |
| Globalene® SI4201 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |