Ghaed ABS/PC GAC 244
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Ghaed Basir Petrochemicals Co. |
| Trademark: | Ghaed ABS/PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QNynyI_Ghaed-ABS-PC-GAC-244.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC/ABS Alloy : Non Reinforced Grade Classification: General purpose>Injection grade Characteristic: Injection grade, high impact Resistance Application: GAC 244 is an unreinforced PC/ABS alloy which offers good impact strength and high heatresistance. Especially, metal plating is very easy with GAC 244. So GAC 244 could be used outdoorhousing which need metal plating such as, automotive door handle, lamp housing, etc |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/21.6 kg) | 35 to 45 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 to 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 23°C) | > 44.1 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C) | > 90 | % | ASTM D638 |
| Flexural Modulus 3(23°C) | > 1770 | MPa | ASTM D790 |
| Flexural Strength 4(23°C) | > 73.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 5 | > 38 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 115 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 95.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | < 0.10 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Nozzle Temperature | 260 to 270 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C | |
| Injection Rate | Slow-Moderate |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | 2.8 mm/min |
| 5 . | 6.4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene P254-01UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Vibrathane® 6007 | Chemtura | PUR-Ester/TDI | Vibrathane® |
| NORDEL™ IP 3720P | The Dow Chemical Company | EPDM | NORDEL™ |
| Clyrell EC2340 | LyondellBasell Industries | PP Impact Copolymer | Clyrell |
| GERMAMID 6 HV | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |