Jackdaw PP ER76NT6354
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | Jackdaw PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QNuan7_Jackdaw-PP-ER76NT6354.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jackdaw PP ER76NT6354 is a Polypropylene product filled with 30% glass fiber. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 0.30 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 6500 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 150 | MPa | ISO 178 |
| Break | 150 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 185 | °C | ASTM D2117, ISO 1218 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 204 A FR UV | RTP Company | Nylon 6 | RTP |
| SILVER® PE 1011.RDH | Guangdong Silver Age Sci & Tech. Co., Ltd | LDPE | SILVER® |
| Ultralast™ PE952 | Chemtura | PUR-Ether/PPDI | Ultralast™ |
| Karina WHITE PVC COMPOUND -E 839-10/158-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sumiliteresin® PR-50395 | SBHPP | Phenolic | Sumiliteresin® |