Staramide BS6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Staramide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QNmpUh_Staramide-BS6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Staramide BS6 is a 30 % Glass Bead Reinforced Polyamide 6 Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 1.0 to 1.5 | % | Internal Method |
| Water Absorption (Saturation, 23°C) | 6.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4200 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 65.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 10 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 4100 | MPa | ISO 178 |
| Flexural Stress | 108 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 3(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 195 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 85.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | 215 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 5.0E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 6.0E-5 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Tested by E2P) | HB | UL 94 | |
| Oxygen Index | 24 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 to 85.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 |
| 4 . | 120*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® 5030 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Homopolymer | POLYPRO® |
| Axpoly® r-PP52 1000 | Axion Polymers | PP Copolymer | Axpoly® |
| Flontech® FT-BRR40-2 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| KPOL-PP K-PPH 1.80 | KPOL Chem Co. | PP Homopolymer | KPOL-PP |
| Lupolen 4261 A IM | LyondellBasell Industries | HDPE | Lupolen |