TECHNYL® C 216 V30 BLUE 2234 CF Datasheet,Nylon 6,Solvay Engineering Plastics-SHANGHAI SUSHENG

Message
TECHNYL® C 216 V30 Blue 2234CF is a polyamide 6, reinforced with 30% of glass fibre, for injection moulding. This grade has good mechanical properties and offering an excellent combination between thermal and mechanical properties.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Features	Good liquidity Good demoulding performance
Uses	Power/other tools Sporting goods General
Agency Ratings	EC 1907/2006 (REACH) UL QMFZ2
Appearance	Black Grey Natural color
Forms	Particle
Processing Method	Injection molding
Resin ID (ISO 1043)	PA6-GF30

Physical	Dry	Conditioned	Unit	Test Method
Density	1.36	--	g/cm³	ISO 1183/A
Water Absorption				ISO 62
23°C, 24 hr	1.1	--	%	ISO 62
Equilibrium, 23°C, 50% RH	2.2	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	9600	6400	MPa	ISO 527-2/1A
Tensile Stress (Break, 23°C)	145	94.0	MPa	ISO 527-2/1A
Tensile Strain (Break, 23°C)	2.1	3.7	%	ISO 527-2
Flexural Modulus (23°C)	7000	4600	MPa	ISO 178
Flexural Stress (23°C)	205	135	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	25	40	kJ/m²	ISO 179/1eU

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	218	--	°C	ISO 75-2/Bf
1.8 MPa, not annealed	200	--	°C	ISO 75-2/Af
Melting Temperature	222	--	°C	ISO 11357-3

Flammability	Dry	Conditioned		Test Method
Flame Rating (1.6 mm)	HB	--		UL 94

Injection	Dry	Unit
Drying Temperature	80	°C
Suggested Max Moisture	0.20	%
Rear Temperature	230 - 235	°C
Middle Temperature	235 - 240	°C
Front Temperature	240 - 250	°C
Mold Temperature	60 - 90	°C

Injection instructions
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Injection instructions

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For reinforced polyamide, Solvay recommends the use of steel with a high content of Carbon and purified for polishing to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Solvay Engineering Plastics
Trademark:	TECHNYL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	QNgUzF_TECHNYLC216V30BLUE2234CF.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
tefabloc® TO 628	Mitsubishi Chemical Performance Polymers, Inc.	SEBS	tefabloc®
Nipoflex® 625	TOSOH Corporation	EVA	Nipoflex®
ACCUCOMP™ CP0408L	ACLO Compounders Inc.	PP Copolymer	ACCUCOMP™
DOWLEX™ 2042G	The Dow Chemical Company	LLDPE	DOWLEX™
Ekalon® 20 E II S	Sattler KunststoffWerk GmbH	PC	Ekalon®