Sup-tech P706
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Shanghai Suptech Engineering Plastics Co. Ltd. |
| Trademark: | Sup-tech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QN8sQQ_Sup-tech-P706.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Sup-tech P706 is a Polypropylene product filled with 30% glass fiber. It can be processed by injection molding and is available in Asia Pacific. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | DIN 53479 |
| Melt Mass-Flow Rate (MFR) | 2.0 to 6.0 | g/10 min | DIN 53735 |
| Molding Shrinkage | 0.010 | % | DIN 53464 |
| Water Absorption (23°C, 24 hr) | 0.040 | % | DIN 53495 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 70.0 | MPa | DIN 53455 |
| Tensile Strain (Break) | 2.0 | % | DIN 53452 |
| Flexural Modulus | 4000 | MPa | DIN 53457 |
| Flexural Stress | 90.0 | MPa | DIN 53457 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 12 | kJ/m² | DIN 53453 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | DIN 53461 | ||
| 0.45 MPa, Unannealed | 145 | °C | |
| 1.8 MPa, Unannealed | 125 | °C | |
| Melting Temperature | 170 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Electric Strength | 17 | kV/mm | DIN 53481 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 185 to 240 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-747R | CHI MEI CORPORATION | ABS | POLYLAC® |
| SLOVASTER® B FRN 3 | Plastcom | PBT | SLOVASTER® |
| AIE PP 80G4 | Asia International Enterprise (Hong Kong) Limited | PP, Unspecified | AIE PP |
| EXCELINK 2600B | JSR Corporation | TPV | EXCELINK |
| IROGRAN® A 85 D 5001 DP | Huntsman Corporation | TPU-Polyester | IROGRAN® |