Kinta NI6000
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Kinta Technology (Hong Kong) Co., Ltd. |
| Trademark: | Kinta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QMo5FZ_KintaNI6000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Kinta NI6000 is a polyamide 6 (nylon 6) product,. It is available in the Asia-Pacific region. The main characteristics are: flame retardant/rated flame. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.00 mm) | 0.80 - 1.3 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 112 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 45.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 160 | % | ASTM D638 |
| Flexural Modulus 3 | 1300 | MPa | ASTM D790 |
| Flexural Strength 4 | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 70.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 52.0 | °C | ASTM D648 |
| Melting Temperature | 225 | °C | DSC |
| CLTE - Flow | 7.0E-5 - 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dissipation Factor 5(23°C, 1 MHz) | 0.030 | ASTM D150 | |
| Arc Resistance | 130 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.2 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 100 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 210 - 230 | °C | |
| Middle Temperature | 220 - 240 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 60 - 80 | °C | |
| Injection Pressure | 100 - 160 | MPa |
| Note Message | |
|---|---|
| 1 . | 10 mm/min |
| 2 . | 10 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 60% RH |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teldene® H03BPM | National Petrochemical Industries Company (NATPET) | PP Homopolymer | Teldene® |
| TEKNIFLEX® VA10300 | Tekni-Films, a div of Tekni-Plex | Film, PVC/PCTFE | TEKNIFLEX® |
| SUMILITE® PVC VSL-4610-N | Sumitomo Bakelite Co., Ltd. | PVDC | SUMILITE® PVC |
| Vipel® F764-BTX-00 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| SABIC® LLDPE MG200024 | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |