NEFTEKHIM PP 1432C (D50S)
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Nizhnekamskneftekhim Inc. |
| Trademark: | NEFTEKHIM PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QM7zL6_NEFTEKHIM-PP-1432C-D50S-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Product obtained by polymerization of propylene in presence of complex organic metal catalysts. It incorporates increased long-term thermal stability, thermaloxidative degradation resistance when PP is produced, processed and PP-made articles are exploited. Improved antistatic properties to produce articles. Application: molded and extruded technical articles, sheets and profiles, extrusion, blow molding. Technical requirements: TU 2211-136-05766801-2006 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | |
| Apparent Density | 0.48 to 0.52 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/5.0 kg | 0.50 to 0.90 | g/10 min | |
| 230°C/2.16 kg | 0.30 to 0.50 | g/10 min | |
| 230°C/5.0 kg | 1.2 to 1.9 | g/10 min | |
| Ash Content | 0.025 to 0.050 | % |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Thermal Creep Temperature 1 | 90 to 96 | °C | |
| Thermal-oxidative Deterioration (150°C) | 3.1 | month |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 82 to 95 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 33.0 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 11 | % | ASTM D638 |
| Flexural Modulus | 1200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Vicat Softening Temperature 2 | 150 to 154 | °C |
| Note Message | |
|---|---|
| 1 . | at load 0.46 H/mm² |
| 2 . | in liquid medium under force 10 H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SE-320P | SHIN-A T&C | Epoxy | SHIN-A |
| Arnite® TV4 260 SN | DSM Engineering Plastics | PBT | Arnite® |
| Kingfa PA66-R0N | Kingfa | Nylon 66 | Kingfa |
| Karina MBPP GREEN 4000/141-IE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Bergadur™ PB40 G30 | PolyOne Corporation | PBT | Bergadur™ |