TECHNYL® A 217 BLACK 61 Datasheet,Nylon 66,Solvay Engineering Plastics-SHANGHAI SUSHENG

Message
TECHNYL ® A 217 Black 61 is an unreinforced polyamide 66, heat stabilized, standard viscosity, for injection moulding. This grade offers all the primary properties of unreinforced polyamide 66. In addition it has improved resistance to high temperature and it can be used for components which have to withstand mid term temperature stresses.

General Information
Additive	heat stabilizer
Features	Heat Stabilized - Inorganic Electroplating Good liquidity Good demoulding performance
Uses	Electrical/Electronic Applications Connector Application in Automobile Field
Agency Ratings	EC 1907/2006 (REACH) EN 45545 NF F 16-101 UL QMFZ2
RoHS Compliance	RoHS compliance
Appearance	Black Natural color
Forms	Particle
Processing Method	Injection molding
Resin ID (ISO 1043)	PA66

Physical	Dry	Conditioned	Unit	Test Method
Density	1.14	--	g/cm³	ISO 1183/A
Water Absorption				ISO 62
23°C, 24 hr	1.3	--	%	ISO 62
Equilibrium, 23°C, 50% RH	2.9	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	3500	1700	MPa	ISO 527-2/1A
Tensile Strength
Yield, 23°C	85.0	--	MPa	ASTM D638
Yield, 23°C	85.0	60.0	MPa	ISO 527-2/1A
Fracture, 23°C	50.0	40.0	MPa	ISO 527-2/1A
Tensile Strain
Yield, 23°C	4.5	10	%	ISO 527-2
Fracture, 23°C	30	--	%	ASTM D638
Fracture, 23°C	20	200	%	ISO 527-2
Flexural Modulus
23°C	3500	--	MPa	ASTM D790
23°C	3100	1450	MPa	ISO 178
Flexural Strength
23°C	125	--	MPa	ASTM D790
23°C	130	80.0	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	4.5	11	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	No Break	No Break		ISO 179/1eU
Notched Izod Impact
23°C	80	--	J/m	ASTM D256
23°C	4.0	10	kJ/m²	ISO 180
Unnotched Izod Impact Strength (23°C)	No Break	No Break		ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, not annealed	220	--	°C	ASTM D648
0.45 MPa, not annealed	210	--	°C	ISO 75-2/Bf
1.8 MPa, not annealed	75.0	--	°C	ASTM D648, ISO 75-2/Af
Melting Temperature	262	--	°C	ISO 11357-3

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	1.0E+15	1.0E+14	ohms	IEC 60093
Volume Resistivity	1.0E+15	1.0E+16	ohms·cm	IEC 60093
Dielectric Strength (2.00 mm)	25	22	kV/mm	IEC 60243-1
Relative Permittivity	2.90	3.20		IEC 60250
Dissipation Factor	0.030	0.080		IEC 60250
Comparative Tracking Index				IEC 60112
Solution a	600	600	V	IEC 60112
Solution B	450	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
1.6 mm	V-2	--		UL 94
3.2 mm	V-2	--		UL 94
Glow Wire Flammability Index				IEC 60695-2-12
0.8 mm	650	--	°C	IEC 60695-2-12
1.6 mm	650	--	°C	IEC 60695-2-12
Glow Wire Ignition Temperature (1.6 mm)	650	--	°C	IEC 60695-2-13
Oxygen Index	26	--	%	ISO 4589-2
French Fire Index	F2	--		NF F16-101
French Smoke Index	I3	--		NF F16-101

Injection	Dry	Unit
Drying Temperature	80	°C
Suggested Max Moisture	0.20	%
Rear Temperature	265 - 275	°C
Middle Temperature	270 - 280	°C
Front Temperature	280 - 285	°C
Mold Temperature	60 - 80	°C

Injection instructions
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For unfilled polyamide, Solvay recommends the use of high alloy steel with a weak chromium content. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Injection instructions

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: For unfilled polyamide, Solvay recommends the use of high alloy steel with a weak chromium content. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm). For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature of 90°C to 120°C with an optimum at 105°C. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Category:	Nylon 66 , Polyamide 66
Manufacturer:	Solvay Engineering Plastics
Trademark:	TECHNYL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	QKSs71_TECHNYLA217BLACK61.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Radilon® AGV 50 Black	Radici Plastics	Nylon 66	Radilon®
VESTAMID® E E62-S3	Evonik Industries AG	Nylon 12	VESTAMID® E
KOPLA PA66 KDT1030	KOPLA Co., Ltd.	Nylon 66	KOPLA PA66
Jam PE 25525	Jam Petrochemical Company	LLDPE	Jam PE
POLYFLAM® RIPP 374 ND CS1 5V	A. Schulman Europe	PP Copolymer	POLYFLAM®