POLYFLAM® RMMK 125
| Category: | ABS+Nylon , Acrylonitrile Butadiene Styrene + Nylon |
| Manufacturer: | A. Schulman Europe |
| Trademark: | POLYFLAM® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QHOZ7e_POLYFLAM-RMMK-125.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame-retardant ABS/PA blend; without PBDE; high stress crack resistance |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.30 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 12.0 | -- | cm³/10min | ISO 1133 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2500 | 940 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 52.0 | 29.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 3.0 | 16 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 9.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 12 | 21 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 113 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 60.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 190 | -- | °C | ISO 306/A50 |
| -- | 156 | -- | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | -- | IEC 60695-10-2 | |
| RTI Elec | UL 746 | |||
| 1.50 mm | 60.0 | -- | °C | UL 746 |
| 3.00 mm | 60.0 | -- | °C | UL 746 |
| RTI Imp | UL 746 | |||
| 1.50 mm | 60.0 | -- | °C | UL 746 |
| 3.00 mm | 60.0 | -- | °C | UL 746 |
| RTI (1.50 mm) | 60.0 60.0 | -- | °C | UL 746 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index | 200 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate | ISO 3795 | |||
| 1.50mm, automatic fire extinguishing | 0.0 | -- | mm/min | ISO 3795 |
| 3.00mm, automatic fire extinguishing | 0.0 | -- | mm/min | ISO 3795 |
| Flame Rating | UL 94, IEC 60695-11-10, -20 | |||
| 1.50 mm | V-0 | -- | UL 94, IEC 60695-11-10, -20 | |
| 3.00 mm | V-0 | -- | UL 94, IEC 60695-11-10, -20 | |
| 2.00 mm | 5VA | -- | UL 94, IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 0.750 mm | 960 | -- | °C | IEC 60695-2-12 |
| 1.50 mm | 960 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 750 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 750 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 31 | -- | % | ISO 4589-2 |
| Additional Information |
|---|
| 干燥 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 230 | °C | |
| Middle Temperature | 240 | °C | |
| Front Temperature | 250 | °C | |
| Nozzle Temperature | 260 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 80.0 - 150 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 5.00 - 10.0 | MPa | |
| Cushion | < 5.00 | mm | |
| Screw Speed | mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| YUNGSOX® PP 3204 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| Xuchuan XCS-2015S | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Abstron IMGS 20 | Bhansali Engineering Polymers Limited | SAN | Abstron |
| INSPIRE™ TF1302 | Trinseo | PP, Unspecified | INSPIRE™ |
| KOPA® KN133G30 | Kolon Plastics, Inc. | Nylon 6 | KOPA® |