Hytrel® RS 40F5 NC010
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® RS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QGyraG_Hytrel-RS-40F5-NC010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 40 Shore D, Renewably Sourced, Medium Viscosity Polyester Elastomer |
| General Information | |
|---|---|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/2.16 kg) | 9.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.70 | % | |
| Across Flow : 80°C, 48 hr | 0.80 | % | |
| Flow | 0.90 | % | |
| Flow : 80°C, 48 hr | 1.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 37 | ||
| Shore D, 15 sec | 33 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 45.0 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Break | 25.0 | MPa | |
| 5.0% Strain | 2.10 | MPa | |
| 10% Strain | 3.50 | MPa | |
| 50% Strain | 6.70 | MPa | |
| Tensile Strain (Break) | > 300 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 800 | % | ISO 527-2 |
| Flexural Modulus | 50.0 | MPa | ISO 178 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| Across Flow | 100 | kN/m | |
| Flow | 100 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | No Break | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -95.0 | °C | ISO 974 |
| Ductile / Brittle Transition Temperature | -95.0 | °C | ISO 6603-2 |
| Melting Temperature 1 | 190 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 2.1E-4 | cm/cm/°C | |
| Transverse | 2.0E-4 | cm/cm/°C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | IEC 60695-11-10, -20 | |
| Oxygen Index | 20 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Effective Thermal Diffusivity | 0.0544 | cSt |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Formolene® 2315N | Formosa Plastics Corporation, U.S.A. | PP Copolymer | Formolene® |
| EPO-TEK® E3037 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| HiFill FR® PA6/6 FR HS | Techmer Engineered Solutions | Nylon 66 | HiFill FR® |
| MAJORIS DE278 | AD majoris | PP, Unspecified | MAJORIS |
| REV Materials 8011-003 | REV Materials | PP, Unspecified | REV Materials |