Badamid® LA70 GF30 TM-Z2
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QGeVkM_Badamid-LA70-GF30-TM-Z2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Chemical very tough modified 30% glass fibres reinforced injection moulding grade |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.33 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 4.7 to 5.3 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.3 to 1.7 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus 1(23°C) | 8500 | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Break, 23°C) | 140 | 100 | MPa | ISO 527-2/5 |
| Tensile Strain 3(Break, 23°C) | 3.5 | 6.0 | % | ISO 527-2/5 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | -- | kJ/m² | |
| 23°C | 19 | 26 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 85 | -- | kJ/m² | |
| 23°C | 90 | 95 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 15 | 18 | kJ/m² | |
| 23°C | 17 | 20 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 4 | 260 | -- | °C | ISO 3146 |
| CLTE | DIN 53752 | |||
| Flow | 2.5E-5 to 3.5E-5 | -- | cm/cm/°C | |
| Transverse | 6.0E-5 to 7.0E-5 | -- | cm/cm/°C | |
| Maximum Service Temperature | IEC 60216 | |||
| -- 5 | 105 | -- | °C | |
| -- | 220 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Relative Permittivity (1 MHz) | 3.50 | 5.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.014 | 0.16 | IEC 60250 | |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm | HB | -- | ||
| 1.60 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 10 K/min |
| 5 . | 20000 H |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS-351Ss | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| Innothane® IE-3082 | Innovative Polymers, Inc. | TSU | Innothane® |
| LNP™ THERMOCOMP™ PX92248 compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| ESTOPLAST EP 1500GY11 | Ester Industries Ltd. | PBT | ESTOPLAST EP |
| Sumikon® PM-9750 | SBHPP | Phenolic | Sumikon® |