EMERGE™ PC 8702-15 (NA)
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QGdNFm_EMERGEPC870215NA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 8702 Advanced Resin is an ignition-resistant, 20% glass reinforced polycarbonate resin. This resin does not contain chlorine or bromine additives. It is a medium flow PC resin with a mold release system, intended for applications requiring high stiffness. EMERGE PC 8702 has a UL94 V-0 rating at 1.5 mm. Main Characteristics:
Applications:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.20 - 0.40 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 4000 | MPa | ASTM D638 |
| Tensile Strength (Break, 3.20 mm, Injection Molded) | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 4.0 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 145 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 140 | °C | ASTM D648 |
| 1.8 MPa, annealed | 143 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.0E+14 | ohms | ASTM D257 |
| Volume Resistivity (1.80 mm) | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 27 | kV/mm | ASTM D149 |
| Dielectric Constant (1.60 mm, 1 MHz) | 3.10 | ASTM D150 | |
| Comparative Tracking Index (3.00 mm) | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 1(1.5 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 288 - 316 | °C | |
| Mold Temperature | 79 - 116 | °C |
| Note Message | |
|---|---|
| 1 . | This rating is not intended to reflect the danger caused by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 800 AR 15 | RTP Company | Acetal (POM) Copolymer | RTP |
| TEKAFIN™ P730G30 | Mando Advanced Materials Co., Ltd. | PP, Unspecified | TEKAFIN™ |
| KOPA® KN133G30BL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Karina WHITE PVC COMPOUND -E 836-10/176-CR | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| SQUARE® LSR1929-50AH/BH | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |