REPOL® B550MN
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QGdKZF_REPOL-B550MN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Repol B550MN is recommended for use in Injection Moulding processes where high flow and medium impact strength are required. It is an ideal material to use in appliance parts, automotive compounds, grilled and thin wall products. Repol B550MN contains nucleating agent. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 55 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 24.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, Injection Molded) | 7.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Injection Molded) | 1150 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 65 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, Injection Molded) | 105 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Talcoprene® OC3030 CM GRIGIO313 | SO.F.TER. SPA | PP, Unspecified | Talcoprene® |
| DOW™ HDPE NG7005 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| CELLOMER® 2100D | Microcell Composite Company | SBS | CELLOMER® |
| EVAL™ FP104B | EVAL Europe nv | EVOH | EVAL™ |
| TECACOMP® PA66 CF30 black 9103 | Ensinger GmbH | Nylon 66 | TECACOMP® |