Keyflex® BT 3047D
| Category: | TPC-ET , Thermoplastic Copolyester Elastomer |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Keyflex® BT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QFvBal_Keyflex-BT-3047D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description Fast Molding, Medium Modulus Application Injection Parts for Lesuire & Sports |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 44 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 2.00 mm) | 28.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 2.00 mm) | 600 | % | ASTM D638 |
| Flexural Modulus 3(6.40 mm) | 137 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 6.40 mm | No Break | ||
| 23°C, 6.40 mm | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 215 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (CTI) 4 | 600 | V | UL 746 |
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Rear Temperature | 215 to 235 | °C | |
| Middle Temperature | 220 to 240 | °C | |
| Front Temperature | 225 to 245 | °C | |
| Nozzle Temperature | 225 to 245 | °C | |
| Processing (Melt) Temp | 215 to 245 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Cylinder Zone 1 Temp. | 215 to 235 | °C | |
| Cylinder Zone 2 Temp. | 225 to 245 | °C | |
| Cylinder Zone 3 Temp. | 225 to 245 | °C | |
| Cylinder Zone 4 Temp. | 225 to 245 | °C | |
| Adapter Temperature | 225 to 245 | °C | |
| Melt Temperature | 215 to 245 | °C | |
| Die Temperature | 215 to 235 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 15 mm/min |
| 4 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTV-2 XP-636 | Silicones, Inc. | Silicone Rubber, RTV-2 | RTV-2 |
| Ranger PBT PBT-201-G10 272 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| TEKNIFLEX® PXA 12300 | Tekni-Films, a div of Tekni-Plex | Film, Copolyester/PCTFE | TEKNIFLEX® |
| DOMAMID® 66G50HR | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| IROSTIC® S 8735 | Huntsman Corporation | TPU, Unspecified | IROSTIC® |