Elastollan® 1154D
| Category: | TPU-Polyether , Thermoplastic Polyurethane Elastomer (Polyether) |
| Manufacturer: | BASF Corp. Thermoplastic Polyurethanes |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QFfv7R_Elastollan-1154D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Elastollan® 1154D exhibits excellent abrasion resistance, toughness, transparency, very good low temperature flexibility, hydrolytic stability and fungus resistance. It has excellent damping characteristics and outstanding resistance to tear propagation. Elastollan® 1154D conforms to the FDA food contact regulations as described in book 21, section 177.2600 for wet food contact applications. Elastollan® 1154D also has NSF Standard 61 "Water Contact Material" certification. Elastollan® 1154D is supplied uncolored in diced form. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.16 | g/cm³ | ASTM D792 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 54 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (2.20 mm, Injection Molded) | 152 | MPa | ASTM D412 |
| Flexural Modulus (2.20 mm, Injection Molded) | 165 | MPa | ASTM D790 |
| Taber Abrasion Resistance | 60.0 | mg | ASTM D1044 |
| Abrasion - DIN | 30 | mm³ | DIN 53516 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Point - DMA | 127 | °C | Internal Method |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain, 2.20 mm | 26.2 | MPa | |
| 300% Strain, 2.20 mm | 45.5 | MPa | |
| Tensile Strength (2.20 mm) | 48.3 | MPa | ASTM D412 |
| Tensile Elongation (Break, 2.20 mm) | 410 | % | ASTM D412 |
| Tear Strength 1(2.20 mm) | 210 | kN/m | ASTM D624 |
| Compression Set | ASTM D395B | ||
| 23°C, 22 hr | 40 | % | |
| 70°C, 22 hr | 50 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -16.0 | °C | Internal Method |
| Vicat Softening Temperature | 138 | °C | ASTM D1525 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 120 | °C | |
| Drying Time | 2.0 to 3.0 | hr | |
| Suggested Max Moisture | 0.030 | % | |
| Rear Temperature | 210 to 230 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 210 to 230 | °C | |
| Nozzle Temperature | 220 to 240 | °C |
| Note Message | |
|---|---|
| 1 . | Die C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 SI 4 | RTP Company | PC | RTP |
| Sup-tech C9706 | Shanghai Suptech Engineering Plastics Co. Ltd. | PC | Sup-tech |
| Vydyne® R543H NT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| DURANEX® 361SA | Polyplastics Co., Ltd. | ABS+PBT | DURANEX® |
| Karina CLEAR PVC COMPOUND -E 70/206-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |