Urochem 134 Datasheet,Urea Formald,Chemiplastica, Inc.-SHANGHAI SUSHENG

Urochem 134

Category:	Urea Formald , Urea Formaldehyde
Manufacturer:	Chemiplastica, Inc.
Trademark:	Urochem
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	QF3I3e_Urochem-134.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Urea- formaldehyde resins with melamine resin fortified with highly refined cellulose as filler, and further modified with minor amounts of special purpose additives, pigments, cure regulators and lubricants. The Urochem 134 Moulding Compounds can be supplied in an almost unlimited range of colours from translucent light pastels to black. Moulded parts are free from odour; UV stable with good moisture resistance. Hard, glossy and scratch resistant surface. Excellent chemical resistance. Fats, oils and common organic solvents like alcohol and acetone do not attack moulded parts which are also resistant to surfactants and weak bases. They will withstand attack from weak acids for a shorter duration. Excellent electrical properties (arc quenching, tracking, flame resistance). Oxygen index of 30% is achieved without the use of external flame retardants. No halogens are present in the composition. Compliant with the requirements of widely used material specifications for amino compounds: BS 1322 type UF A10 () DIN 7708 type 131.5 () ISO 2112 type UF A10 () UL certified () included in ISO 14527 Fields of application: Optimized for use primarily in the thermoset injection moulding process. Particularly well suited for electrical components such as sockets, lamp holders, and domestic circuit breakers.

Message

Urea- formaldehyde resins with melamine resin fortified with highly refined cellulose as filler, and further modified with minor amounts of special purpose additives, pigments, cure regulators and lubricants.

The Urochem 134 Moulding Compounds can be supplied in an almost unlimited range of colours from translucent light pastels to black.

Moulded parts are free from odour; UV stable with good moisture resistance.

Hard, glossy and scratch resistant surface.

Excellent chemical resistance. Fats, oils and common organic solvents like alcohol and acetone do not attack moulded parts which are also resistant to surfactants and weak bases. They will withstand attack from weak acids for a shorter duration.

Excellent electrical properties (arc quenching, tracking, flame resistance). Oxygen index of 30% is achieved without the use of external flame retardants. No halogens are present in the composition.

Compliant with the requirements of widely used material specifications for amino compounds:
BS 1322 type UF A10 (*)
DIN 7708 type 131.5 (*)
ISO 2112 type UF A10 (*)
UL certified
(*) included in ISO 14527

Fields of application: Optimized for use primarily in the thermoset injection moulding process.

Particularly well suited for electrical components such as sockets, lamp holders, and domestic circuit breakers.

General Information
Filler / Reinforcement	Fiber filler
Additive	Lubricant Unspecified additive
Features	Moisture resistance Highlight Solvent resistance Good UV resistance Updatable resources Recyclable materials Good electrical performance Scratch resistance Good chemical resistance alkali resistance Alcohol resistance Oil resistance The smell is low to none Lubrication Halogen-free High hardness
Uses	Electrical components
RoHS Compliance	RoHS compliance
Appearance	Available colors
Forms	Particles
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.50	g/cm³	ISO 1183
Molding Shrinkage			ISO 2577
-- ¹	0.80 - 1.1	%	ISO 2577
--	0.80 - 1.0	%	ISO 2577
Water Absorption		mg	ISO 62

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress (Yield)	> 55.0	MPa	ISO 527-2
Flexural Stress	> 100	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	> 1.6	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength	> 8.0	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	> 130	°C	ISO 75-2/A
8.0 MPa, not annealed	> 90.0	°C	ISO 75-2/C

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.1E+11	ohms	IEC 60093
Volume Resistivity	> 1.1E+11	ohms·cm	IEC 60093
Dielectric Constant	5.00		DIN 53483
Comparative Tracking Index	> 600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating	V-0		UL 94
Glow Wire Flammability Index ²	960	°C	IEC 707
Oxygen Index	> 30	%	ASTM D2863

Injection	Nominal Value	Unit
Nozzle Temperature	95.0 - 115	°C
Mold Temperature	145 - 160	°C
Injection Pressure	70.0 - 150	MPa
Holding Pressure	30.0 - 80.0	MPa
Back Pressure	10.0 - 14.0	MPa

Injection instructions
Barrel inlet temp: 70 to 85°CHydraulic injection pressure: 50 to 170 barHydraulic backpressure: 7 to 11 barInjection speed: 100 to 200 cm³/s

Note Message
1 .	Post-shrink
2 .	180 sec

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X3491	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
PRIMALENE WPP514E18	Southern Polymer, Inc.	EVA	PRIMALENE
APEX® 90-A472R-55-NT	Teknor Apex Company	PVC, Flexible	APEX®
Delta PPR-1LG80 HSL	Delta Polymers	PP Homopolymer	Delta
KOPA® KN187	Kolon Plastics, Inc.	Nylon 6	KOPA®

Resin Grade

Manufacturer