Lupoy®GP5200 is a polycarbonate + acrylonitrile butadiene styrene (PC + ABS) material, and its filler is 20% glass fiber reinforced material. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Typical application areas include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm, Injection Molded) | 0.10 - 0.30 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, Injection Molded) | 116 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm, Injection Molded) | 93.2 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm, Injection Molded) | 2.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm, Injection Molded) | 5300 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm, Injection Molded) | 137 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, unannealed, 6.40mm, injection molding) | 115 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 235 - 255 | °C | |
| Front Temperature | 250 - 265 | °C | |
| Nozzle Temperature | 250 - 265 | °C | |
| Processing (Melt) Temp | 235 - 265 | °C | |
| Back Pressure | 0.0196 - 0.0588 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02% |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Thermylene® P7-60FG-0790 | Asahi Kasei Plastics North America Inc. | PP, Unspecified | Thermylene® |
| Borealis PE FS1470 | Borealis AG | HDPE | Borealis PE |
| BP RPP 1009 GK | Buckeye Polymers, Inc. | PP, Unspecified | BP |
| Grilamid® 2D 25 W 20 HL X black 9992 | EMS-GRIVORY | Nylon 6/12 | Grilamid® |
| 3M™ Dyneon™ Fluoroelastomer FE 5840Q | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |