Polygrade® PET B3 G30 NTLA010 PG303
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Polygrade® PET |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QCgG0w_Polygrade-PET-B3-G30-NTLA010-PG303.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polygrade® PET B3 G30 NTLA010 PG303 is a Polyethylene Terephthalate (PET) material filled with 30% glass fiber. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Polygrade® PET B3 G30 NTLA010 PG303: Flame Rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.55 to 1.57 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.25 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 157 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.6 | % | ASTM D638 |
| Flexural Modulus | 8950 | MPa | ASTM D790 |
| Flexural Strength | 233 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 223 | °C | ASTM D696 |
| Melting Temperature | 253 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 20 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | < 0.020 | % | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | > 95.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® CP-13066 NAT XRD1 | Teknor Apex Company | TPE | Monprene® |
| Terblend® N NM-13 | INEOS Styrolution Group GmbH | ABS+Nylon | Terblend® N |
| Bergamid™ A70 G14 TM-X NC060 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Karina BLACK PVC COMPOUND TR-781-48/1-B-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 8925-85 Blue 8366 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |