4PROP® 25C21115 IUV2
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | 4Plas |
| Trademark: | 4PROP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QCcFnw_4PROP-25C21115-IUV2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 4PROP 25C21115 IUV2 is a MFI 15 15% Talc Filled Impact & UV Stabilised Copolymer Polypropylene |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.00 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Hardness- Shore A | 62.0 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 20.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 20 | % | ISO 527-2/5 |
| Flexural Modulus 1(23°C) | 2.00 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 32 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 107 | °C | ISO 75-2/B |
| Melting Temperature 2 | 165 | °C | ISO 11357 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 200 - 240 | °C | |
| Mold Temperature | 20.0 - 50.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 40.0 - 80.0 | MPa | |
| Screw Speed | 400 | rpm |
| Injection instructions |
|---|
| Feed Throat Temperature: 20 - 60 °CBack Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 10 K/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 2686 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| RELENE® 45GP004 | Reliance Industries Limited | HDPE | RELENE® |
| Silmar® SIL93BE-1586 | Interplastic Corporation | Polyester, TS | Silmar® |
| EUROPLEX® Sheet F3 | Evonik Industries AG | PC | EUROPLEX® Sheet |
| PLUSTEK RA103 | Polyram Ram-On Industries | Nylon 66 | PLUSTEK |