Adell Polyamide BH-38
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Adell Plastics, Inc. |
| Trademark: | Adell Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QCBrPY_Adell-Polyamide-BH-38.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adell Polyamide BH-38 is a polyamide 6 (nylon 6) material that contains 40% mineral fillers. This product is available in North America,. The typical application field of Adell Polyamide BH-38 is: automobile industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.80 - 1.2 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.70 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 90 | ASTM D785 | |
| Class r | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 86.2 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 13 | % | ASTM D638 |
| Flexural Modulus | 5170 | MPa | ASTM D790 |
| Flexural Strength | 124 | MPa | ASTM D790 |
| Compressive Strength | 159 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 40 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 182 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 143 | °C | ASTM D648 |
| Melting Temperature | 216 - 227 | °C |
| Additional Information |
|---|
| Elongation at Break, ASTM D638: 10 to 15%Specific Gravity, ASTM D792: 1.47 to 1.49 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 271 - 282 | °C | |
| Front Temperature | 266 - 277 | °C | |
| Nozzle Temperature | 249 - 260 | °C | |
| Processing (Melt) Temp | 249 - 271 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Injection Pressure | 4.83 - 13.8 | MPa | |
| Injection Rate | Slow |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell Polyamide AR-13 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Bayblend® FR3000 HI | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| Escorene™ Ultra UL 05540EH2 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Sylvin 2997-80 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® AKV 30 G H2.0 SR1 900051 | LANXESS GmbH | Nylon 66 | Durethan® |