PPR PA603
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Premier Plastic Resins, Inc. |
| Trademark: | PPR |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QBgIbe_PPR-PA603.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Reprocessed Nylon 6 13% Glass Fiber Reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 82.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus - Tangent | 3790 | MPa | ASTM D790 |
| Flexural Strength | 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 64 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 213 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 193 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.0 - 82.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 238 - 282 | °C | |
| Middle Temperature | 249 - 293 | °C | |
| Front Temperature | 249 - 293 | °C | |
| Nozzle Temperature | 243 - 288 | °C | |
| Processing (Melt) Temp | 254 - 299 | °C | |
| Mold Temperature | 66.0 - 93.0 | °C | |
| Injection Pressure | 14.0 - 103 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 10.0 - 83.0 | MPa | |
| Back Pressure | 0.00 - 1.00 | MPa | |
| Cushion | 6.35 - 12.7 | mm |
| Injection instructions |
|---|
| Screw Speed: Slow-ModerateDecompression: 3.81 to 7.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P1960T | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Queo™ 0219 | Borealis AG | Plastomer | Queo™ |
| CONATHANE® CE-1175 | Cytec Industries Inc. | PUR, Unspecified | CONATHANE® |
| ICORENE® 2550 YELLOW 2538 | ICO Polymers EMEA, A Division of A. Schulman | LLDPE | ICORENE® |
| PHOENIX™ 8901 | Phon Tech Industrial Company | TPE | PHOENIX™ |