VALOX™ K4560 resin
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | VALOX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QBI9tz_VALOXK4560resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass reinforced PBT. Impact modified, high flow, hydrolytically stable. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.60 - 0.80 | % | Internal method |
| Transverse flow : 3.20mm | 1.0 - 1.2 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 8840 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 112 | MPa | ASTM D638 |
| Fracture 3 | 107 110 112 115 102 | MPa | ASTM D638 |
| Fracture 4 | 96.0 | MPa | ASTM D638 |
| Fracture | 120 | MPa | ISO 527-2/5 |
| Tensile Elongation 5 | ASTM D638 | ||
| Yield | 3.0 4.0 | % | ASTM D638 |
| Fracture | 2.5 3.0 2.2 4.0 | % | ASTM D638 |
| Flexural Modulus | |||
| 50.0mm span 6 | 8000 7500 7100 7200 7400 | MPa | ASTM D790 |
| -- 7 | 7400 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 175 | MPa | ISO 178 |
| Fracture, 50.0mm span 8 | 173 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 9 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 820 | J/m | ASTM D4812 |
| 23°C 10 | 52 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact (23°C, Total Energy) | 6.10 7.56 8.81 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 220 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 200 | °C | ASTM D648 |
| Vicat Softening Temperature | 204 | °C | ISO 306/B120 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Fiber Content | 30 | % | ISO 3451 |
| Flexural Strain 11 | 4.2 4.5 4.2 4.0 | % | ASTM D790 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 60.0 - 76.7 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Suggested Shot Size | 40 - 80 | % | |
| Rear Temperature | 238 - 254 | °C | |
| Middle Temperature | 243 - 260 | °C | |
| Front Temperature | 249 - 266 | °C | |
| Nozzle Temperature | 243 - 260 | °C | |
| Processing (Melt) Temp | 249 - 266 | °C | |
| Mold Temperature | 65.6 - 87.8 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 50 - 80 | rpm | |
| Vent Depth | 0.025 - 0.038 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 1.3 mm/min, 50 mm span |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 300 TFE 5 SI 2 | RTP Company | PC | RTP |
| ResMart Ultra TPU 95A ES | ResMart | TPU-Polyester | ResMart Ultra |
| SMOKEGUARD™ O 209 NATURAL | AlphaGary | Polyolefin, Unspecified | SMOKEGUARD™ O |
| Braskem PE SGF4950 | Braskem | HDPE | Braskem PE |
| SABIC® LLDPE M500026 | Saudi Basic Industries Corporation (SABIC) | LLDPE | SABIC® LLDPE |