Tenopom® POM B3 ST PRTA010 PR325 MSP
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Tenopom® POM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QB9LZ9_Tenopom-POM-B3-ST-PRTA010-PR325-MSP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyacetal copolymer natural, super tough, highly impact modified, easily processed and indicated for the injection of parts which require good resistance to fatigue and friction. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 1.5 to 1.6 | % | ASTM D955 |
| Water Absorption (Saturation) | 0.80 | % | ASTM D570 |
| Ash Content | 1.4 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1650 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 43.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 16 | % | ASTM D638 |
| Flexural Modulus | 1550 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 140 | °C | |
| 1.8 MPa, Unannealed | 75.0 | °C | |
| Vicat Softening Temperature | 160 | °C | ASTM D1525 2 |
| Melting Temperature | 166 | °C | ASTM D2117 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 160 to 180 | °C | |
| Mold Temperature | 70.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| U-polymer UM-8430RG | UNITIKA Plastics Division | Polyarylate | U-polymer |
| APEX® 3703-80NT1 | Teknor Apex Company | PVC, Flexible | APEX® |
| Ducor® DE2348T | Ducor Petrochemicals BV | PP Impact Copolymer | Ducor® |
| PEARLSTICK® D40-70/33 | Lubrizol Advanced Materials, Inc. | TPU-Polyester | PEARLSTICK® |
| Kepital® TX-11H | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |