Hifax CA45G
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QAqAP9_Hifax-CA45G.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hifax CA45G medium melt flow, 820 MPa flexural modulus, reactor grade thermoplastic elastomeric olefin (TEO) resin has a very good balance of properties and excellent moldability. It was designed primarily for molded-in color automotive exterior components and is based on material from Basell's Spheripol process. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.890 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 16.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2 |
| Flexural Modulus | 820 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -40°C | 7.0 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 63.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 43.0 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 100°C) | 1.0E-4 | cm/cm/°C | ASTM E228, ISO 11359-2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solprene® 4302 | Dynasol Elastomers | SBS | Solprene® |
| 4MID® 9A22140 HR | 4Plas | Nylon 66 | 4MID® |
| Akulon® S223-HG6 | DSM Engineering Plastics | Nylon 66 | Akulon® |
| ELASTOSIL® R 401/55 | Wacker Chemie AG | Silicone | ELASTOSIL® R |
| Lytex 4143 | Quantum Composites Inc. | Epoxy | Lytex |