Kepital® MF3025
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QAG1eM_Kepital-MF3025.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A medium-high viscosity grade for general injection molding. It was reinforced milled glass fiber, and so suitable for parts requiring low warpage than those of the FG grade by reinforcing short glass fiber. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.58 | g/cm³ | ASTM D792 |
| -- | 1.59 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 17 | g/10 min | ASTM D1238 |
| -- | 16 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 2.00 mm | 1.3 | % | ASTM D955 |
| 3.00 mm | 1.3 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 60% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield, 23°C | 65.0 | MPa | ASTM D638 |
| Yield, 23°C | 78.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break, 23°C | 4.0 | % | ASTM D638 |
| Break | 4.9 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 5000 | MPa | ASTM D790 |
| 23°C | 5530 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 113 | MPa | ASTM D790 |
| 23°C | 129 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.8 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (3.20 mm) | 42 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 156 | °C | ASTM D648 |
| Peak Melting Temperature | 165 | °C | ASTM D3418 |
| CLTE - Flow (20 to 80°C) | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | ASTM D257, IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257, IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makropol® PC B3 HF UV FR CLRA015 PC312 | Petropol Industry and Trade of Polymers LTDA | PC | Makropol® PC |
| Ranger PBT PBT-403-M-G15 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Hanwha Total PP BJ522 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Impact Copolymer | Hanwha Total PP |
| Sylvin 4299-70 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 2997-90 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |