InSphere® 0513FR-P
| Category: | PS (EPS) , Expanded Polystyrene |
| Manufacturer: | Synthos S.A. |
| Trademark: | InSphere® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | QA05cR_InSphere-0513FR-P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
InSphere® type 0513FR-P is self-extinguishing expandable polystyrene (EPS) with a reduced water absorption and reduced amount of hydrocarbon blowing agent. The materials are formed by spherical polystyrene particles that contain a flame retardant system and a hydrocarbon blowing agent. Their surface is treated against gluing during processing and the formation of electrostatic charge. Due to the content of halogenated flame retardant and the residual blowing agent, the product is unsuitable for objects intended for direct contact with food. InSphere® 0513FR-P is mainly used for perimetric and skirting boards; production of shaped parts with wall thickness above 10 mm (e.g. shipping packaging for glass and electrical goods, building bricks, floor and roof shaped parts); production of smaller blocks with higher density or cutted profiles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Density 1 | 0.02 to 0.04 | g/cm³ | Internal Method |
| Moisture Content | < 10000 | ppm | Internal Method |
| Particle Size - >95% between | 500 to 1000 | µm | Internal Method |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Reaction to Fire | |||
| -- | B1 | DIN 4102 | |
| -- | Class E | EN 13501-1 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blowing Agent | < 5.0 | wt% | Internal Method |
| Note Message | |
|---|---|
| 1 . | The typical bulk density indicates values obtained during single-step pre-foaming on continuous pre-foaming devicesLower values of bulk density can be achieved only after multiple pre-expansion. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unichem 8512N-02 | Colorite Polymers | PVC, Flexible | Unichem |
| Hanwha Total PP GH42M | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| King Pearl® N Series | Loyal Chemical | PS (EPS) | King Pearl® |
| LNP™ THERMOCOMP™ MC002 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |
| LNP™ STAT-KON™ ZE0039 compound | SABIC Innovative Plastics | Polyphenylene, Unspecified | LNP™ STAT-KON™ |