TECACOMP® PA66 TC white 3924
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q94hgv_TECACOMPPA66TCwhite3924.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | |
| Apparent Density | 0.79 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 40 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 26.5 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 0.67 | % | ISO 294-4 |
| Flow | 0.36 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.3 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 13000 | MPa | ISO 527-2/50 |
| Tensile Stress | 105 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 1.5 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 25 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 252 | °C | ISO 75-2/A |
| Glass Transition Temperature | 50.0 | °C | DIN 53765 |
| Melting Temperature | 255 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 45°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Flow : 70 to 120°C | 2.5E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 45°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 70 to 120°C | 7.5E-5 | cm/cm/°C | ISO 11359-2 |
| Specific Heat | 1090 | J/kg/°C | DIN EN 821 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 1.5 | W/m/K | DIN EN 821 |
| -- 2 | 3.5 | W/m/K | DIN EN 821 |
| Service Temperature | |||
| long term | 120 | °C | |
| short term | 180 | °C | |
| Thermal Diffusivity | DIN EN 821 | ||
| In-plane | 1.60 | cSt | DIN EN 821 |
| Through-plane | 0.700 | cSt | DIN EN 821 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+12 | ohms | DIN EN 61340 |
| Volume Resistivity | 3.6E+13 | ohms·cm | DIN EN 61340 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Processing (Melt) Temp | 260 - 295 | °C | |
| Mold Temperature | 100 - 150 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYLOY® NG-1020NM | Nytex Composites Co., Ltd. | Nylon 6 | NYLOY® |
| Advanced Composites ADX-5007 | Advanced Composites, Inc. | TPO | Advanced Composites |
| Fiberfil® PP-61/CC/20 | Fiberfil® Engineered Plastics Inc. | PP Copolymer | Fiberfil® |
| Karina WHITE PVC COMPOUND -E 855-10/150-ERYB-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 50-8779 | Lehmann & Voss & Co. | PC | LUVOCOM® |