AKROMID® B3 GF 50 black (4907)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q94EdH_AKROMID-B3-GF-50-black-4907-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 GF 50 black (4907) is a 50% glass fibre reinforced polyamide 6 with very high rigidity and strength Applications are mainly components in mechanical engineering and in the automotive industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.56 | g/cm³ | ISO 1183 |
| Spiral Flow | 46.0 | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.90 | % | |
| Flow | 0.20 | % | |
| Water Absorption (Saturation, 23°C) | 4.5 to 5.1 | % | ISO 62 |
| Humidity Absorption - 62% RH (70°C) | 1.3 to 1.6 | % | ISO 1110 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content | 50 | % | ISO 1172 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 17000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 240 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 16000 | MPa | ISO 178 |
| Flexural Stress 2 | 360 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 90 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 100 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 220 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 220 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 185 | °C | ISO 75-2/C |
| Melting Temperature 3 | 220 | °C | DIN EN 11357-1 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 1.1E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 9.4E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (1.60 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Toler PS PS8000 | Toler Chemical, Inc | PS (GPPS) | Toler PS |
| Vinnolit® E 68 FO | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| ESTAPROP KUR 4000 CH/TD | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| Lucalen A2920M Q225 | LyondellBasell Industries | LDPE | Lucalen |
| LEXAN™ LXS1210 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |