ELEVATE™ EF532AA
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | ELEVATE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q8DSPg_ELEVATEEF532AA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake ELEVATE™ EF532AA is an ethylene vinyl acetate copolymer with 12% VA. EF532AA is designed as a heat seal layer for co-extruded cast film applications that require excellent optics and low heat seal initiation. Application/Uses
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.933 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 12.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm, cast film | 72.4 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, cast film | 79.3 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 25 µm, extruded film | 24.8 | MPa | ASTM D882 |
| TD : Broken, 25 µm, extruded film | 21.4 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 25 µm, extruded film | 400 | % | ASTM D882 |
| TD : Broken, 25 µm, extruded film | 800 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Cast Film) | 130 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 70.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 93.9 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45, 25.4 µm, cast film) | 80 | ASTM D2457 | |
| Haze (25.4 µm, Cast Film) | 2.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties shown are typical as measured on 1.0 mil cast film. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WPP PP PPH4TF4-Black | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| GATONE™ 5300PF | Solvay Specialities India Private Limited (SSIPL) | PEEK | GATONE™ |
| ESTALUX 5513 | Cossa Polimeri S.r.l. | MABS | ESTALUX |
| Karina WHITE PVC COMPOUND -E 822-10/148-CRB-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 9058-90UV Black 214 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |