PBT, non-reinforced, injection molding,Extrusion, food contact

General Information
Features	Compliance of Food Exposure
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Extrusion Injection molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.30	g/cm³	ISO 1183
Apparent Density	0.80	g/cm³	ISO 60
Melt Volume-Flow Rate (MVR) (260°C/2.16 kg)	14.0	cm³/10min	ISO 1133
Molding Shrinkage
Vertical flow direction : 260°C, 3.00mm ¹	1.8	%	ISO 2577
Vertical flow direction : 150°C, 48 hours, 3.00mm ²	0.50	%	ISO 294-4
Flow direction : 260°C, 3.00mm ³	1.8	%	ISO 2577
Flow direction : 150°C, 48 hours, 3.00mm ⁴	0.50	%	ISO 2577
Water Absorption			ISO 62
Saturated, 23°C	0.50	%	ISO 62
Equilibrium, 23°C, 50% RH	0.20	%	ISO 62
Viscosity Number (Reduced Viscosity)	140.0	ml/g	ISO 1628

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	120	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	2600	MPa	ISO 527-2/1
Tensile Stress (Yield, 23°C)	55.0	MPa	ISO 527-2/50
Tensile Strain (Yield, 23°C)	4.0	%	ISO 527-2/50
Nominal Tensile Strain at Break (23°C)	> 50	%	ISO 527-2/50
Tensile Creep Modulus			ISO 899-1
1 hr	2200	MPa	ISO 899-1
1000 hr	1300	MPa	ISO 899-1
Flexural Modulus ⁵(23°C)	2650	MPa	ISO 178/A
Flexural Stress ⁶
3.5% strain	75.0	MPa	ISO 178/A
23°C	85.0	MPa	ISO 178
Flexural Strain at Flexural Strength ⁷(23°C)	6.0	%

Flammability	Nominal Value	Unit	Test Method
Burning Behavior ⁸	passed		ISO 3795

Additional Information	Nominal Value		Test Method
Electrolytical Corrosion	A 1		IEC 60426
Gottfert Melt Viscosity (260°C)	570165 1/s		Internal method
ISO Shortname	PBT, G, 11-030		ISO 7792

Injection	Nominal Value	Unit	Test Method
Residual Moisture Content	0.0 - 0.020	%	Karl Fisher

Films	Nominal Value	Unit	Test Method
Film Puncture Force ⁹	4280	N	ISO 6603-2

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	< 10	kJ/m²	ISO 179/1eA
23°C	< 10	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	200	kJ/m²	ISO 179/1eU
23°C	No Break		ISO 179/1eU
Notched Izod Impact			ISO 180/1A
-40°C	< 10	kJ/m²	ISO 180/1A
-30°C	< 10	kJ/m²	ISO 180/1A
23°C	< 10	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength			ISO 180/1U
-30°C	160	kJ/m²	ISO 180/1U
23°C	No Break		ISO 180/1U

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	160	°C	ISO 75-2/B
1.8 MPa, not annealed	60.0	°C	ISO 75-2/A
8.0 MPa, not annealed	45.0	°C	ISO 75-2/C
Vicat Softening Temperature	180	°C	ISO 306/B50
Ball Pressure Test (190°C)	Pass		IEC 60695-10-2
Melting Temperature ¹⁰	225	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : 23 to 55°C	1.2E-4	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	1.3E-4	cm/cm/°C	ISO 11359-2
Thermal Conductivity (23°C)	0.25	W/m/K	ISO 8302

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength (23°C, 1.00 mm)	30	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
23°C, 100 Hz	3.40		IEC 60250
23°C, 1 MHz	3.20		IEC 60250
Comparative Tracking Index			IEC 60112
Solution a	600	V	IEC 60112
Solution B	425	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.800 mm	HB		UL 94
1.60 mm	HB		UL 94
Glow Wire Flammability Index (2.00 mm)	750	°C	IEC 60695-2-12
Oxygen Index ¹¹	24	%	ISO 4589-2

Injection	Nominal Value	Unit	Test Method
Drying Temperature - Circulation Dryer	120	°C
Drying Time - Circulation Dryer	4.0 - 8.0	hr

Note Message
1 .	150x150x3; MT 80°C; 600 Bar
2 .	150x105x3
3 .	150x150x3; MT 80°C; 600 Bar
4 .	150x150x3
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	Pull Rate: 2 mm/min; 50% RH
8 .	US-FMVSS302
9 .	-30°C
10 .	10°C/min
11 .	Procedure A

Resin Grade	Manufacturer	Category	Trademark
RONFALIN® GGT07	A. Schulman Europe	ABS	RONFALIN®
MonoSol® M8630 - 3 mil	MonoSol, LLC	PVOH	MonoSol®
EPO-TEK® E3001-6	Epoxy Technology Inc.	Epoxy	EPO-TEK®
INDURE™ X210A	LyondellBasell Industries	TPO (POE)	INDURE™
Plenco 04349 (Transfer)	Plastics Engineering Co.	Phenolic	Plenco