AvaSpire® AV-621 CF30
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | AvaSpire® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Q72zRa_AvaSpire-AV-621-CF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AvaSpire AV-621 CF30 is a AvaSpire AV-621 30% carbon fiber reinforced brand. Dimensional stability and warpage resistance are better than those of 30% carbon fiber reinforced PEEK. Toughness and impact strength are higher than PEEK (polyetheretherketone). Among all AV 621 grades, AV-621 CF30 has the highest strength, rigidity and fatigue resistance. Moreover, the resin also retains most of the useful key properties of carbon fiber reinforced PEEK, including chemical resistance, fatigue resistance, and long-term thermal oxidation stability. The excellent balance of various properties of the AV-621 CF30 enables it to be used for a wide range of purposes in all walks of life, including healthcare, transportation, electronics and chemical processing. The material can be easily melted on standard equipment. The melt processability of AV-621 CF30 is very close to that of 30% CF-enhanced PEEK. The low fluidity AV-621 CF30 brand is very suitable for extrusion purposes and has the properties of AV-651 CF30. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.42 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage 1 | ASTM D955 | ||
| Flow : 3.18mm | 0.0 - 0.20 | % | ASTM D955 |
| Transverse flow : 3.18mm | 0.90 - 1.1 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 101 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 17200 | MPa | ASTM D638 |
| -- | 23300 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | |||
| Yield | 196 | MPa | ISO 527-2/1A/5 |
| -- 3 | 181 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Fracture 4 | 2.2 | % | ASTM D638 |
| Fracture | 2.2 | % | ISO 527-2/1A/5 |
| Flexural Modulus | |||
| -- | 15100 | MPa | ASTM D790 |
| -- | 21300 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 276 | MPa | ASTM D790 |
| -- | 296 | MPa | ISO 178 |
| Compressive Strength | 152 | MPa | ASTM D695 |
| Shear Strength | 91.0 | MPa | ASTM D732 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -- | 69 | J/m | ASTM D256 |
| -- | 9.6 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| -- | 640 | J/m | ASTM D4812 |
| -- | 39 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 5(1.8 MPa, Annealed, 3.20 mm) | 210 | °C | ASTM D648 |
| Glass Transition Temperature | 160 | °C | ASTM D3418 |
| Peak Melting Temperature | 340 | °C | ASTM D3418 |
| CLTE - Flow (-50 to 50°C) | 5.0E-6 | cm/cm/°C | ASTM E831 |
| Specific Heat | DSC | ||
| 50°C | 1350 | J/kg/°C | DSC |
| 200°C | 1810 | J/kg/°C | DSC |
| Thermal Conductivity | 0.35 | W/m/K | ASTM E1530 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (400°C, 1000 sec^-1) | 790 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 366 | °C | |
| Middle Temperature | 371 | °C | |
| Front Temperature | 377 | °C | |
| Nozzle Temperature | 382 | °C | |
| Processing (Melt) Temp | 366 - 388 | °C | |
| Mold Temperature | 149 - 177 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Injection instructions |
|---|
| 保压压力：最低值 |
| Note Message | |
|---|---|
| 1 . | 5" x 0.5" x 0.125" bars |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 5.0 mm/min |
| 5 . | 200°C,2 hours |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UBESTA 3030 JI5L | UBE Engineering Plastics, S.A. | Nylon 12 | UBESTA |
| NAXALOY® 774 | MRC Polymers, Inc. | PC+ABS | NAXALOY® |
| CONATHANE® EN-2552 | Cytec Industries Inc. | PUR, Unspecified | CONATHANE® |
| KRALASTIC® SRE | Nippon A&L Inc. | ABS | KRALASTIC® |
| INVISION™ VX 5075UI | A. Schulman Inc. | TPV | INVISION™ |